Supported Molybdenum Carbide and Nitride Catalysts for Carbon Dioxide Hydrogenation

M. Abou Hamdan (1) , A. Nassereddine (1) , R. Checa (2) , M. Jahjah (1) , C. Pinel (3) , L. Piccolo (2) , N. Perret (3)

1 IRCELYON - Institut de recherches sur la catalyse et l'environnement de Lyon
2 CATREN - IRCELYON-Catalyse Hétérogène pour la Transition Energétique
3 CDURABLE - IRCELYON-C'Durable

Catalysts based on molybdenum carbide or nitride nanoparticles (2–5 nm) supported on titania were prepared by wet impregnation followed by a thermal treatment under alkane (methane or ethane)/hydrogen or nitrogen/hydrogen mixture, respectively. The samples were characterized by elemental analysis, volumetric adsorption of nitrogen, X-ray diffraction, and aberration-corrected transmission electron microscopy. They were evaluated for the hydrogenation of CO2 in the 2–3 MPa and 200–300°C ranges using a gas-phase flow fixed bed reactor. CO, methane, methanol, and ethane (in fraction-decreasing order) were formed on carbides, whereas CO, methanol, and methane were formed on nitrides. The carbide and nitride phase stoichiometries were tuned by varying the preparation conditions, leading to C/Mo and N/Mo atomic ratios of 0.2–1.8 and 0.5–0.7, respectively. The carbide activity increased for lower carburizing alkane concentration and temperature, i.e., lower C/Mo ratio. Enhanced carbide performances were obtained with pure anatase titania support as compared to P25 (anatase/rutile) titania or zirconia, with a methanol selectivity up to 11% at 250°C. The nitride catalysts appeared less active but reached a methanol selectivity of 16% at 250°C.CO(2)hydrogenation

Keywords: CO 2 hydrogenation; carbide; nitride; supported catalysts; TiO 2; ZrO 2

Domains: Catalysis

M. Abou Hamdan, A. Nassereddine, R. Checa, M. Jahjah, C. Pinel, et al.. Supported Molybdenum Carbide and Nitride Catalysts for Carbon Dioxide Hydrogenation. Frontiers in Chemistry, 2020, 8, pp.452. ⟨10.3389/fchem.2020.00452⟩. ⟨hal-02903129⟩